Ascione, Laura
(2013)
Synthesis and Characterization of Hyperbranched Polyesters for Special Uses.
[Tesi di dottorato]
| Tipologia del documento: |
Tesi di dottorato
|
| Lingua: |
English |
| Titolo: |
Synthesis and Characterization of Hyperbranched Polyesters for Special Uses |
| Autori: |
| Autore | Email |
|---|
| Ascione, Laura | ascione.laura@gmail.com |
|
| Data: |
1 Aprile 2013 |
| Numero di pagine: |
161 |
| Istituzione: |
Università degli Studi di Napoli Federico II |
| Dipartimento: |
Ingegneria Chimica, dei Materiali e della Produzione Industriale |
| Scuola di dottorato: |
Ingegneria industriale |
| Dottorato: |
Ingegneria dei materiali e delle strutture |
| Ciclo di dottorato: |
25 |
| Coordinatore del Corso di dottorato: |
| nome | email |
|---|
| Mensitieri, Giuseppe | mensitie@unina.it |
|
| Tutor: |
| nome | email |
|---|
| Carfagna, Cosimo | carfagna@unina.it | | Ambrogi, Veronica | ambrogi@unina.it |
|
| Data: |
1 Aprile 2013 |
| Numero di pagine: |
161 |
| Parole chiave: |
Hyperbranched Polyester |
| Settori scientifico-disciplinari del MIUR: |
Area 03 - Scienze chimiche > CHIM/05 - Scienza e tecnologia dei materiali polimerici
Area 09 - Ingegneria industriale e dell'informazione > ING-IND/22 - Scienza e tecnologia dei materiali |
| Aree tematiche (7° programma Quadro): |
NANOSCIENZE, NANOTECNOLOGIE, MATERIALE E PRODUZIONE > Materiali |
[error in script]
[error in script]
| Depositato il: |
08 Apr 2013 09:54 |
| Ultima modifica: |
22 Apr 2016 01:00 |
| URI: |
http://www.fedoa.unina.it/id/eprint/9342 |
Abstract
“Life is branched” was the motto of a special issue of Macromolecular Chemistry and Physics on “Branched Polymers”, indicating that branching is of similar importance in the world of synthetic macromolecules as it is in nature. This work is focus on the synthetic approaches used to prepare highly branched polymers, diluting the branching with linear polymer chains by creating increasingly complex linear-branched hybrid systems. Structural characterization of hyperbranched samples was made by NMR spectroscopy and MALDI-TOF mass spectrometry. The structure-to-thermal relationship was also investigated through TGA, DSC and WAXD analyses. The complex architecture and compact structures, the absence of chain entanglements, and a large number of functional end-groups yield these materials good low migration polymeric plasticizers for flexible PVC compounds, high performance toughening agents for epoxy resin matrix and excellent crystallization inhibitors and drug delivery systems for an innovative antimalarial drug, artemisinin.